Technical literature
China Zhongliqi Quick-drying offset sublimation ink
China Zhongliqi Quick-drying offset sublimation ink
Brand |
Zhongliqi |
Color |
Magenta, yellow, green, black |
Single net |
1kg or 2kg |
Tinting strength |
95(%) |
Degree of fineness |
3-5(um) |
Viscosity |
20-80(S) |
Dry |
≤10 |
Fixing speed |
≤1(min) |
Applicable |
Polyester fabric,Nylon fabric,Acrylic fabric |
Fluidity |
≥100(mm) |
Type |
Sublimation ink |
PH |
6-7 |
-Quick-drying ink printing materials: Coated paper, coating paper, offset paper and all kinds of paper
-Offset ink Features: solid speed, good stability on the machine, clear dot reproduction, excellent ink-water balanc.
-To adjust the liquidity available 6 # Printing Mexican oil, the amount of 0-5%;
-While reducing the viscosity and viscosity, can add 52-94, the amount of 0-5%.
- Notice: It apply to offset printing machine.Speed is below 8000r/h.Before using the printing plate you should Play the sample first ,if there is no deviation and then determine the comp Engraving and Printing. Because the sublimation ink for gas coloring, it is not ordinary printing according to the proportion .
-- Quick-drying offset printing ink Printed list of the desired temperature (for reference)
Name of fabric |
Transfer temperature |
pressure |
Time |
Polyester fabric |
205°C~220°C |
0.5kg/cm2 |
10~30 seconds |
Polyester deformation fabric low elastic |
195°C~205°C |
0.5kg/cm2 |
30 seconds |
Triacetate fabrics |
190°C~200°C |
0.5kg/cm2 |
30~40 seconds |
Nylon fabric |
195°C~205°C |
0.5kg/cm2 |
30~40 seconds |
Acrylic fabric |
200°C~210°C |
0.5kg/cm2 |
30 seconds |
Two acetate fiber fabric |
185°C |
0.5kg/cm2 |
15~20 seconds |
Polypropylene nitrile |
190°C~220°C |
0.5kg/cm2 |
10~15 seconds |
- Dyeing solid (grade)
exposure to sunlight |
red |
yellow |
green |
black |
5-6 |
6 |
4 |
4 |